Haosteel is professional manufacturer and supplier&$nbsp;of 321 hot rolled stainless steel plate. Quality guaranteed, On-ti∑me delivery, After-sales warranty.
|
Standard: |
ASTM A240 A666 |
|
Grade: |
321 |
|
Delivery: |
Cold rolled Hot rolled |
|
Surface: |
Black/Bright/2B/BA/ NO.1/Hairline/Mirror |
|
Thickness: |
2.5-100mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15 days in common |
Description:
Type 321 is an austenitic chromium-nickel stainless steel containing Titanium which is recommen☆ded for parts fabricated by welding which cannot subsequently be annealed.Type 321 is a♦ stabilized austenitic stainless steel similar to type 304 but wi±th a titanium addition . This titanium addition reduces or prevents carbide¶ precipitation during welding and in 800 – 1500°F (427 – 816°C) service. It also improves the elevated temperature properties of the aλlloy. Type 321 provides excellent resistance to oxidation and corrosion and φpossesses good creep strength.
Chemical composition:
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Ti |
|
≤ 0.08 |
≤ 0.75 |
≤ 2.00 |
≤ 0.045 |
≤ 0.03 |
17.0 - 19.0 |
9.0 - 12.0 |
5(C=N)~0.7 |
Physical Properties:
Annealed:
Ultimate Tensile Strength – 75KSI min (515 MPA min)
Yield Strength (0.2% Offset) –30 KSI min (205 MPA min)
Elongation – 40% min
Hardness – HRB95max (217HV max)
Applications:
Aircraft collector rings, exhaust stacks, carburetεor air intensifier tubes, exhaust manifolds, flexible couplings, jet engine σparts, mufflers, pressure vessels, tubing, fasteners, flexible δmetal hose and bellows.
Heat Treatment:
Type 321 is non hardenable by heat treatment. It c an only be hardened by cold working.
Cold Forming:
321 can be readily formed and drawn. Like most other auste±nitic stainless steels, type 321 work hardens and may← require annealing after severe forming.
Corrosion Resistance:
321 has excellent corrosion resistance equivalent to type 302 or 304 in the annealed condition and superior if ≠a weldment in these grades has not been post-weld <annealed or if the application involves service in the 800°→F – 1600°F range.