2205 cold rolled stainless steel sheet
2205 cold rolled stainless steel sheet
Haosteel is professional manufacturer and supplier of ↑2205 cold rolled stainless steel sheet. Quality&n₹bsp;guaranteed, On-time delivery, After-sales warranty.
|
Standard: |
ASTM A240 A666 |
|
Grade: |
2205/S31803/F51/1.4462 |
|
Delivery: |
Cold rolled Hot rolled |
|
Surface: |
Black/Bright/2B/BA/ NO.1/Hairline/Mirror |
|
Thickness: |
0.25-3mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15days in common |
2205 Stainless Steel Sheet,1.4462 Stainless Steel Sheet,S31803 Stai₹nless Steel Sheet,F51 Stainless Steel Sheet
Description:
Material grade: 2205 duplex steelUSA: UNS S31803
German brand : 1.4462 Chinese brand: 00Cr22Ni5Mo3N, F51
2205 (S31803, F51, 1.4462) two-phase stainless steel overview:
2205 (S31803, F51, 1.4462) two-phase steel is a new product successfully developed in 2000. 2φ205 two-phase steel is a kind of two-phase stainless steel with nitrogen added (2205 tγwo-phase steel for short). 2205 two-phase steel is a compound stainless stee§l composed of 21% chromium,2.5% molybdenum and 4.5% nickel-nitrogen allδoy.
The existing 2205 dual-phase steel products include welded pipe, seamless pipe→, steel plate, bar, forging material, strip and so oαn.
Early duplex stainless steels can withstand uniform corrosion and chlorine stress corrosi™on cracking at moderate strength, but their performance is greatly reduced when used in weld&ing situations.
To improve this situation, 2205 two-phase steel is added to nπitrogen, which not only improves corrosion resistance, but also makes the welding condition very® good.
It has high strength, good impact toughness and good overall and local st≤ress corrosion resistance.
The yield strength of 2205 duplex steel is twice that of austenitic stainless steel, a property that allows designers to design products₽ with less weight, giving the alloy a price advantage over 316,317 L.
This alloy is particularly suitable for the temperature range of -50°F/+600°F.
This alloy may also be considered for applications 'beyond this temperature range, but there are some limitat↓ions, especially when applied to welded structures.
Due to the special properties and characteristics of 2205 duplex steel, it is wi≥dely used.
2205 S31803 F51 1.4462 Chemical composition of stainless steel
|
C≤ |
Si≤ |
Mn≤ |
P≤ |
S≤ |
Cr≥ |
Ni≥ |
Mo≥ |
N≤ |
|
0.03 |
1.00 |
2.00 |
0.030 |
0.020 |
21.0-23.0 |
4.5-6.5 |
2.5-3.5 |
0.08-0.20 |
Physical and mechanical properties of duplex stainless steel:
1. 2205 (S31803, F51, 1.4462) dual-phase steel density: 8.0g/cm3¶.
2. 2205 (S31803, F51, 1.4462) two-phase steel tensile str↕ength: σb≥620Mpa.
2205 (S31803, F51, 1.4462) two-phase steel yield strength: σ0.2≥450Mpa
4. Elongation of 22205 (S31803, F51, 1.4462) duplex steel elongation:&delt≤a; ≥25%.
2205 (S31803, F51, 1.4462) two-phase stainless steel corrosion εresistance:
1. Uniform corrosion: due to the chromium content (22%), molybdenum (3%) and nit§rogen content (0.18%) of 2205 dual-phase steel, the corrosion resistance of 2205 is b→etter than 316L and 317L in most environments.
2. Local corrosion resistance: the content of chromium, >molybdenum and nitrogen in 2205 dual-phase steel makes it highly resistant to spot corrosion anφd gap corrosion in oxidizing and acidic solutions.
3, stress corrosion resistance: 2205 dual-phase steel↕ dual-phase microstructure is helpful to improve the stress c™orrosion cracking resistance of stainless steel.
Under certain conditions of temperature, strain, oxygen and chloride, the c"hloride stress corrosion of austenitic stainless steel will occur.
As these conditions are not easily controlled, the use of 304L, 316L and 317L is ←restricted in this respect.
4. Corrosion fatigue resistance: 2205 dual-phase sλteel has high corrosion fatigue strength due to its high strength and corrosion resistanceα.
2205 (S31803, F51, 1.4462) duplex stainless steel structure:
The ideal microstructure of 2205 (S31803, F51, 1.4462) duplex steel can be obtained after soliΩd melt annealing treatment of 1900°/1922°F (1040°/1080°C).
If the heat treatment temperature is higher than 2000°F, it may lead to an increa•se in ferrite composition.
Like other duplex stainless steels, 2205 duplex steels are susceptible to int€ermetallic phase precipitation.
The intermetallic phase precipitated between 1300°F and 1800°F↓, and the precipitation rate was the fastest at 1600°ε;F.
2205 (S31803, F51, 1.4462) duplex stainless steel processing properties:
1. Thermal forming: it is recommended that the forming should be done at✔ a temperature below 600°F.
During the thermoforming process, the whole workpiece shall be heated as a× whole and shall be carried out in a temperature ran ge from 1750°F to 2250°F, at which temperature 2205 duplex steel is very soft.
If the temperature is too high, 2205 duplex steel is prone to thermal teaπring.
Below this temperature, the austenite breaks.
Below 1700°F, the metal meets quickly due to temperature∏ and deformation.
After the thermoforming is completed, it shall be immediately annealed and quenched at a minimu★m temperature of 1900°F to reduce its phase balance, toughness and corrosion resistance.
Stress relief is not recommended, but if it is necessary, t¶he material should be soldered at a minimum temperatu>re of 1900°F, followed by rapid cooling and water quenching.
2. Cold forming: 2205 two-phase steel can be cut and cold formed.
However, due to the high strength and hardness of 2205 duplex↕ steel, it needs to be cold formed more than austenitic steel, and due to its high strengφth, the resilience factor should be fully considered.
3. Heat treatment: 2205 duplex steel shall be annealed at a minimum te×mperature of 1900°F, and then rapidly cooled to water quenching.
This treatment is applied to solid - melt annealing and stress relief.
Stress relief treatment at temperatures below 1900°F can easily lea∑d to the precipitation of harmful metal or non-metal phases.
4. Mechanical machinability: on high-speed machine tools, the feed rate and cutting speed of 2205 dual-phase steel are the same as that of 316L.
If the carbonization knife is used, the cutting speed is reduced by about 20% compared with 31↕6L. The performance of the machine and its components plays a key role here.
5. Welding: the weldability of 2205 alloy is very good.
The performance of 2205 dual phase steel is that the welded metal and thermal deterioration par≥ts still retain the same corrosion resistance, strength and tou€ghness as the base metal.
It is not difficult to weld 2205 two-phase steel, but the weld≈ing procedure should be designed to maintain a good phase balance after welding, so as to avoid the precipitation of harmful metal phase or non-metal phase.
2205 (S31803, F51, 1.4462) duplex stainless steel
2205 dual phase steel applications: neutral chloride environment, oil refinin₽g industry, petrochemical and chemical industry, chemical indust®ry pipeline, oil and gas industry, pulp and paper industry, feδrtilizer industry, urea industry, phosphate fertilizer industr₹y, the water environment, energy and environmental protection industry, light industry and fo"od industry, food and pharmaceutical industry equipment, high strenλgth structure, subsea pipeline, osmosis desalination equipment, desuεlphurization and sulfuric acid plant, Marine engine₽ering fasteners, etc.
2205 (S31803, F51, 1.4462) duplex stainless steel variety specification and supply s₩tatus:
1. Variety classification: 2205 seamless pipe, 2205 steel plate, 2205 rou•nd steel, 2205 forging, 2205 flange, 2205 ring, 2205 welded pipe, 2205 steel belt, 22↔05 wire material and 2205 matching welding material.
2, delivery status: seamless tube: solid solution + acid white, length can be fixed length;
Plate: solid solution, pickling, cutting edge;
Welded pipe: solution acid white +RT% flaw detection∏, forging: annealing + polishing;
Bar by forging rolling state, surface polishing or polishing;
After cold rolling, solid solution soft state, oxide skin delivery;
The silk material shall be delivered in the state of fine polishing in the form of solid solut§ion pickling tray or straight strip.
Product display