304L cold hot rolled stainless steel coil
304L S30403 1.4306 1.4307 cold rolled stainless steel coil
Haosteel is professional manufacturer and supplier of 304L cold rolled stai✘nless steel coil. Quality guaranteed, On-time delivery, After-sales& warranty.
|
Standard: |
ASTM A240 |
|
Grade: |
304L S30403 1.4306 1.4307 |
|
Delivery: |
Cold rolled |
|
Surface: |
2B/2D |
|
Thickness: |
0.25-3mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15days in common |
Description:
Alloy 304L a T-300 series stainless steel austenitic, which has a minimum of 18% chromiu<m and 8% nickel. Type 304L has a carbon maximum is 0.030. It is the s tandard “18/8 stainless” that is commonly found in pans and cooking tools. Alloys ₩304L is the most versatile and widely used alloy in the stainless steel family. Ideal for a wi♣de variety of home and commercial applications, Alloys 304L exhibits excellent corrosion resistan×ce and has a high ease of fabrication, outstanding formability. The austenitic ≤stainless steels are also considered to be the most weldable" of the high-alloy steels and can be welded by all fusion an<d resistance welding processes.
Chemical composition:
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
N |
|
≤ 0.03 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.03 |
18.0 - 20.0 |
8.0 - 10.5 |
≤ 0.10 |
Physical Properties:
Annealed:
Ultimate Tensile Strength – 70 KSI min (485 MP♣A min)
Yield Strength (0.2% Offset) –25 KSI min (170 MPA min)
Elongation – 40% min
Hardness – HRB92 max (210HV max)
Tempered Condition:
The use of chip breakers is advised since the chips can be st•ringy. Stainless steel work harden rapidly, heavy positive feeds, sharp tooling, andπ a rigid set-up should be used.of cut below the work-hardened layer resulting f♦rom the previous passes.
Corrosion Resistance:
At times, alloy 304L may show a lower corrosion rate than the higher carbon Alloy 304; otherwise, the 304, 304L, and 304H may be considered to perform uniformly in most corrosive environmen€ts. Alloy 304L is preferred for use in environments sufficiently corrosive toσ cause intergranular corrosion of welds and heat-affected zones on susceptible alloys.