PRODUCT CENTER
304L cold rolled stainless steel sheet
304L cold rolled stainless steel sheet
Haosteel is professional manufacturer and supplier of 304L cold rol☆led stainless steel sheet. Quality guaranteed, On-time delivery, After-salλes warranty.
|
Standard: |
ASTM A240 A666 |
|
Grade: |
304L |
|
Delivery: |
Cold rolled Hot rolled |
|
Surface: |
Black/Bright/2B/BA/ NO.1/Hairline/Mirror |
|
Thickness: |
0.25-3mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15days in common |
Description:
Alloy 304L a T-300 series stainless steel austenitic, which has a minimum of 18% chromiu♣m and 8% nickel. Type 304L has a carbon maximum is 0.030. It is the standaβrd “18/8 stainless” that is commonly found in pans and cooking tools. Alloys 304L is t≈he most versatile and widely used alloy in the stainless stαeel family. Ideal for a wide variety of home and commercial ♣applications, Alloys 304L exhibits excellent corrosion resis₽tance and has a high ease of fabrication, outstanding formability. The austenitic stainless steels →are also considered to be the most weldable of the high-alloy ste$els and can be welded by all fusion and resistance welding processes.
Chemical composition:
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
N |
|
≤ 0.03 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.03 |
18.0 - 20.0 |
8.0 - 10.5 |
≤ 0.10 |
Physical Properties:
Annealed:
Ultimate Tensile Strength – 70 KSI min (485 MPA min)
Yield Strength (0.2% Offset) –25 KSI min (170 MPA min)
Elongation – 40% min
Hardness – HRB92 max (210HV max)
Tempered Condition:
The use of chip breakers is advised since the chips can be ×stringy. Stainless steel work harden rapidly, heavy positive feeds, Ωsharp tooling, and a rigid set-up should be used.of cut below the work-<hardened layer resulting from the previous passes.
Corrosion Resistance:
At times, alloy 304L may show a lower corrosion rate than the higher carbon Alloy↔ 304; otherwise, the 304, 304L, and 304H may be considered to perform uniformly in most corrosive environments. Alloy 304L is preferred for use in environments §sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones o n susceptible alloys.
Product display