410S hot rolled stainless steel plate
410S hot rolled stainless steel plate
Haosteel is professional manufacturer and&©nbsp;supplier of 410S hot rolled stainless stee≈l plate. Quality guaranteed, On-time delivery, After-sales warαranty.
|
Standard: |
ASTM A240 A666 |
|
Grade: |
410s |
|
Delivery: |
Cold rolled Hot rolled |
|
Surface: |
Black/Bright/2B/BA/ NO.1/Hairline/Mirror |
|
Thickness: |
2.5-100mm |
|
Width: |
1m-3m |
|
Length: |
2m-12m |
|
Mill: |
Tisco, Jisco, Baosteel, etc. |
|
Delivery time: |
15 days in common |
Description:
Haosteel Stainless inventory now includes Alloy 410S (UNS S41008) in sheet, plate a→nd processed flat bar. Tubular products are available upon request. Alloy 410S (UNS S41008≈) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general pur↕pose 12% chromium martensitic stainless steel. The low carbon and a small alloy additi£on minimize austenite formation at high temperatures which res★tricts the alloys ability to harden. 410S remains soft and ductile even when rapidly coo↑led from above the critical temperature. This non-hardenεing characteristic helps prevent cracking when the alloy i∑s exposed to high temperatures or welded. 410S is compλletely ferritic in the annealed condition. It exhibits adequate corrosion resistan₹ce similar to 410 and good oxidation resistance.
Chemical composition:
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
|
≤ 0.08 |
≤ 1.00 |
≤ 1.00 |
≤ 0.04 |
≤ 0.03 |
11.5- 13.5 |
≤ 0.60 |
Physical Properties:
Annealed:
Ultimate Tensile Strength – 64.4KSI min (405 MPA ↕min)
Yield Strength (0.2% Offset) –42 KSI min (205 MPA min)
Elongation – 33% min
Hardness – HRB75max (217HV max)
Corrosion Resistance:
Grade 410 stainless steels are resistant to hot gases, steam, food, mild acids and alkali☆es, fresh water and dry air. These steels obtain maximum corrosion and heat resistaεnce through hardening. However, grade 410 steels are less corrosion resistant than austenitic grades and grade 430 ferr itic alloys containing 17% chromium. Smooth surface finish offers improved performance of steels.
Heat Resistance:
Grade 410 steels have good scaling resistance at temperatures of up to 6γ50°C. However, the mechanical properties of the material will tend to reduce at temperatures ♥ranging from 400 to 580°C.
Forging:
Pre heat carefully, then raise temperature to 1100"-1200°C, hold until temperature is uniform through the steel. Do not forge below 900&de g;C. After forging stainless steel 410 grade, cool slowly in a furnace or warm ashes.
Machining:
Grade 410 steels can be easily machined in highly tempered or annealed conditions. However, it is hard to machine grade 410 steels if they are hardened above 30HRC. Free machining grade 416 is the best alternative.
Applications:
· Bolts, screws, bushings and nuts
· Petroleum fractionating structures
· Shafts, pumps and valves
· Mine ladder rungs
· Gas turbines